This is a composite sheet which incorporate non- Asbestos sealing materials and perforated or flat metal sheet, Either as a core or facing after processing with vulcanization and bonding technologies. The product contains NBR and aramid fiber with good compressibility and recovery, And small stress relaxation. The short duration maximum temperature is up to 400℃ (750℉).
WAG- TL1310 combines non- Asbestos material and perforated carbon steel as a core.
Technical Specifications
Item Names Specification
Density (g/ Cm3) ≥2. 5
Compressibility (%, At 34. 5 MPa) 8- 18
Recovery (%) ≥40
Stress Relaxation (%) ≤30
Ignition lost (%, At 800℃, 1h) ≤15
Fluid Resistance
(at ASTM standard oil #3, 150℃, 5h) Change in Weight (%) ≤30
Change in Thickness(%) ≤20
Fluid Resistance
(at ASTM fuel B, 21- 30 ℃, 5h)
Change in Weight (%) ≤30
Change in Thickness (%) ≤20
WAG3- TL1310 combines non- Asbestos material and perforated metal sheet as facing on both sides.
Technical Specifications
Item Names Specification
Density (g/ Cm3) 3- 4
Compressibility (%, At 34. 5 MPa) 8- 17
Recovery (%) ≥35
Stress Relaxation (%) ≤30
Ignition lost (%, At 800℃, 1h) ≤15
Fluid Resistance
(at ASTM standard oil #3, 150℃, 5h) Change in Weight (%) ≤30
Change in Thickness(%) ≤20
Fluid Resistance
(at ASTM fuel B, 21- 30 ℃, 5h)
Change in Weight (%) ≤30
Change in Thickness (%) ≤20
Related Product Tags:
adhesive strip , Airproof , aluminum strip , bearing seal , Clutch Bearing Seal , body seal , boot seal , brake cup seal , cam ring , hydraulic cartridge , steering cartridge , water cartridge , Absorber Strut Cartridge , cartridge , hino cartridge , toyota cartridge , centrifugal pump , clutch brake