Stainless Steel Shot Metal Abrasive,China Auto Parts,buy Stainless Steel ,Suppliers, Manufacturers, Exporters from gasgoo.com

Home » Product Directory » Material And Equipment » Materials » Metal »

Image for Stainless Steel Shot Metal Abrasive

Stainless Steel Shot Metal Abrasive

Application: Acura, Alfa Romeo, Aston ...
Market Type:After Market
FOB Price: USD 4500USD
Other Price Term: CIF
Payment Terms: L/C, T/T, D/P
Samples: Free
Minimum Order: 1Ton/Tons

Contact Supplier no sign-up required

Add to Favorites

Product Details

Company Profile

Quick Details

Place of Origin:
CHINA
Samples:
Free
Delivery Time:
ABOUT 20 DAYS
Packing:
5kg /Bag Package 40 Bags/ Pallet 18-23 Metric Tons/ Container, Or As Customers Request.
Delivery Port:
XINGANG, CHINA
Max. Production Capacity:
10000T/M
Export Ratio:
91% - 100%
OE Experience:
No

Product Name:Stainless Steel Shot Metal Abrasive

Stainless Steel Shot Metal Abrasive

Application

Acura, Alfa Romeo, Aston Martin, Audi, Aux, Baolong, Bmw, Byd, Cadillac, Chery, Citroen, Dadi, Dodge, Ferrari, Fiat, Ford, Foton, Fuqi, Geely, Gmc, Great Wall, Hafei, Jeep, Jac, Toyota, Toyota, Volkswagen, Volvo, Vw, Wuling

Product Description:

1..standards:AMS 2431, MIL-S-13165C, DIN8201, VDFI8001, SAEJ827, SAEJ441
2.Hardness: 6500 times
3. Surface cleaning,rust removal,blasting
4.Main technical indicators of stainless steel shot

Products	Stainless Steel Shot	Stainless Steel Cut Wire Shot
Shape	Conditioned (Spherical)	As cut (Cylindrical)
Sizes specifications	From 0.2mm to 2.5mm
Standards	In accordance with AMS 2431, MIL-S-13165C, DIN8201, VDFI8001, SAEJ827, SAEJ441 standards
Chemical composition 304Type	Carbon (C)	0.12%
	Manganese (Mn)	2.00%
	Silicon (Si)	1.00%
	Chromium (Cr)	17~19%
	Nickel (Ni)	7~10%
	Sulfur (S)	0.03%
	Phosphorus (P)	0.035%
Microhardness	308~509 HV Vickers 41~59 HRC Rockwell
Tensile intension	490~1520 Mpa
Durability	6500Times (1.0mm, VDFI8001)
Microstructure	Deformed Austenite
Density	7.8 g/cm³
Bulk density	4.7 g/cm³
Note: Part of the 304 Austenite stainless steel shot will convert into Marten site type, getting magnetic through a process of drawing, cutting and rounding.